| 單位：mm 多大彈墊配多大螺栓 以下尺寸僅供參考 特別在意者甚拍 | ||||||||
| 規格 | d | h | H | 每1000件 質量約等kg |
||||
| min | max | 公稱 | min | max | min | max | ||
| 2 | 2.1 | 2.35 | 0.5 | 0.42 | 0.58 | 1 | 1.25 | 0.02 |
| 2.5 | 2.6 | 2.85 | 0.65 | 0.57 | 0.73 | 1.3 | 1.63 | 0.03 |
| 3 | 3.1 | 3.4 | 0.8 | 0.7 | 0.9 | 1.6 | 2 | 0.06 |
| 4 | 4.1 | 4.4 | 1.1 | 1 | 1.2 | 1.4 | 2.6 | 3.25 |
| 5 | 5.1 | 5.4 | 1.3 | 1.2 | 1.4 | 2.6 | 3.25 | 0.26 |
| 6 | 6.1 | 6.68 | 1.6 | 1.5 | 1.7 | 3.2 | 4 | 0.47 |
| 8 | 8.1 | 8.68 | 2.1 | 2 | 2.2 | 4.2 | 5.25 | 1.07 |
| 10 | 10.2 | 10.9 | 2.6 | 2.45 | 2.75 | 5.2 | 6.5 | 2.05 |
| 12 | 12.2 | 12.9 | 3.1 | 2.95 | 3.25 | 6.2 | 7.75 | 3.49 |
| 14 | 14.2 | 14.9 | 3.6 | 3.4 | 3.8 | 7.2 | 9 | 5.47 |
| 16 | 16.2 | 16.9 | 4.1 | 3.9 | 4.3 | 8.2 | 10.25 | 8.09 |
| 18 | 18.2 | 19.04 | 4.5 | 4.3 | 4.7 | 9 | 11.25 | 10.91 |
| 20 | 20.2 | 21.04 | 5 | 4.8 | 5.2 | 10 | 12.5 | 14.95 |
| 22 | 22.5 | 23.04 | 5.5 | 5.3 | 5.7 | 11 | 13.75 | 20.11 |
| 24 | 24.5 | 25.5 | 6 | 5.8 | 6.2 | 12 | 15 | 26.06 |
| 27 | 27.5 | 28.5 | 6.8 | 6.5 | 7.1 | 13.6 | 17 | 37.64 |
| 30 | 30.5 | 31.5 | 7.5 | 7.2 | 7.8 | 15 | 18.75 | 50.73 |
| 化學成分，%,max | ||||||||||
| 組別 | C | Si | Mn | P | S | Cr | Mo | Ni | Cu | 特性 |
| 304-A2 | 0.1 | 1 | 2 | 0.05 | 0.03 | 15-20 | 8-19 | 4 |
加工硬化率適中，適于一般的冷間加工以及伸抽，冷加工性能較好，普遍用于外六角螺釘、螺母以及墊圈產品 |
|
| 316-A4 | 0.08 | 1 | 2 | 0.045 | 0.03 | 16-18.5 | 2-3 | 10-15 | 1 |
加鉬，耐腐蝕能力較304強，特別適用于海水及化學介質，更加的耐腐蝕性及耐孔蝕性。 |
|
注： 1)如鎳含量低于8%,則錳的最小含量必須為5% |
||||||||||
| 機械性能 | |||||||||||
| 類別 | 組別 | 性能等級 | 螺絲直徑 | 抗拉強度mpa/mm2 | 規定非比列伸長應為mpa/mm2 | 斷后伸長量mpa/mm2 | |||||
| 奧氏體 | A2，A4 | 50 |
≤ 39 |
500 | 210 | 0.6d | |||||
| 70 |
≤ 24 |
700 | 450 | 0.4d | |||||||
| 80 |
≤ 24 |
800 | 600 | 0.3d | |||||||